專利名稱(中)	用於電池陽極材料的偏[二]硫亞銻酸銀奈米線及其製備方法
專利名稱(英)	AgSbS2 nanowire as anode materials of battery and a manufacturing method thereof
專利家族	中華民國：I800288
專利權人	國立清華大學 100.00%
發明人	段興宇,何勝峯
技術領域	能源科技

專利摘要(中)
公開一種用於電池陽極材料的偏[二]硫亞銻酸銀奈米線及其製備方法(AgSbS2)，包括以下步驟：(a)將一界面活性劑溶於乙二醇中並在室溫下攪拌以獲得一混合溶液；(b)將硝酸銀、氯化銻、硫乙醯胺同時加入含有該界面活性劑的該混合溶液中並持續攪拌至該混合溶液產生一中間產物為止；(c)將含有該中間產物的該混合溶液加入一水熱反應器中，該混合溶液在該水熱反應器中進行反應、冷卻以形成一沉澱物；以及(d)離心並以乙醇清洗該沉澱物以獲得一偏[二]硫亞銻酸銀奈米線。該偏[二]硫亞銻酸銀奈米線可用於製備電池陽極材料。

專利摘要(中)

公開一種用於電池陽極材料的偏[二]硫亞銻酸銀奈米線及其製備方法(AgSbS2)，包括以下步驟：(a)將一界面活性劑溶於乙二醇中並在室溫下攪拌以獲得一混合溶液；(b)將硝酸銀、氯化銻、硫乙醯胺同時加入含有該界面活性劑的該混合溶液中並持續攪拌至該混合溶液產生一中間產物為止；(c)將含有該中間產物的該混合溶液加入一水熱反應器中，該混合溶液在該水熱反應器中進行反應、冷卻以形成一沉澱物；以及(d)離心並以乙醇清洗該沉澱物以獲得一偏[二]硫亞銻酸銀奈米線。該偏[二]硫亞銻酸銀奈米線可用於製備電池陽極材料。

專利摘要(英)
An AgSbS2 nanowire used as anode materials and a manufacturing method thereof are disclosed. The manufacturing method includes a step (a) of dissolving a surfactant in ethylene glycol with stirring at room temperature to obtain a mixing solution; a step (b) of simultaneously adding silver nitrate, antimony chloride, and thioacetamide in the mixing solution containing the surfactant, and continuously stirring the mixing solution until an intermediate product is produced; a step (c) of transferring the mixing solution containing the intermediate product to a hydrothermal synthesis reactor, wherein the mixing solution reacts and cools in the hydrothermal synthesis reactor to form a precipitate; and a step (d) of centrifuging the mixing solution to collect the precipitate and washing the precipitate with ethanol to obtain the AgSbS2 nanowire. The AgSbS2 nanowire can be used to manufacture anode materials of batteries.

專利摘要(英)

An AgSbS2 nanowire used as anode materials and a manufacturing method thereof are disclosed. The manufacturing method includes a step (a) of dissolving a surfactant in ethylene glycol with stirring at room temperature to obtain a mixing solution; a step (b) of simultaneously adding silver nitrate, antimony chloride, and thioacetamide in the mixing solution containing the surfactant, and continuously stirring the mixing solution until an intermediate product is produced; a step (c) of transferring the mixing solution containing the intermediate product to a hydrothermal synthesis reactor, wherein the mixing solution reacts and cools in the hydrothermal synthesis reactor to form a precipitate; and a step (d) of centrifuging the mixing solution to collect the precipitate and washing the precipitate with ethanol to obtain the AgSbS2 nanowire. The AgSbS2 nanowire can be used to manufacture anode materials of batteries.